material: | FV520B 1.4594 S45000 S143/4/5 Hot Forged And Rolled Stainless Steel Round Bar |
size: | 16.0~450mm, others on request |
delivery state: | annealed, QT |
surface: | black, peeled, machined |
Company Info. |
Wuxi Guanglu Special Steel Co., Ltd |
Verified Supplier |
View Contact Details |
Product List |
FV520B 1.4594 S45000 S143/4/5 Hot Forged And Rolled Stainless Steel
Round Bar
FV520B is a martensitic precipitation hardening stainless steel. It
is similar to the more common
PH stainless grade 17-4PH.
FV520B has useful corrosion resistance in modest corrosion
environments having similar characteristics
to that of austenitic stainless steel grades. It has useful
resistance to some acid conditions and
has low rusting rate in marine and industrial atmospheres.
FV520B has good weldability characteristics when using standard
techniques.
Oxy-acetylene welding is not recommended due to the possible pick
up of carbon.
We recommend you contact your welding consumables supplier who
should provide you full assistance
and information on welding FV520B stainless steel.
Typical applications include pump shafts, impellers, fasteners,
fans, valves, hydraulic equipment
used in oil and gas industries, petrochemical, marine and nuclear
engineering, and aircraft
components such as steam turbine blades.
Chemical composition ( weight % )
Grade | C | Si | Mn | P | S | Cr | Ni | Mo | Cu | Nb |
FV520B | 0.07 max | 0.70 max | 1.00 max | 0.035 max | 0.025 max | 13.20~14.70 | 5.00~6.00 | 1.20~2.00 | 1.20~2.00 | 0.20~0.70 |
Typical Automated Properties
Condition | 0.2% Proof Stress N/mm² | Tensile Strength N/mm² | Elongation % min | Hardness Brinell HB | Izod Joules min |
Primary Hardened 1050º C +2 hours 750-850ºC | - | - | - | 293-341 | - |
Double Overaged 1050º C +2 hours 750-850ºC +2 hours 550ºC | 800 | 925-1090 | 15 | 277-341 | 54 |
Heat treatment
Heat assay temperatures, including amount of heating, cooling and
assimilation times will alter due to factors
such as the appearance and admeasurement of anniversary steel
component.
Added considerations during the calefaction assay action cover the
blazon of furnace, abatement boilerplate
and plan breadth alteration facilities. Amuse argue your
calefaction assay provider for abounding advice on
calefaction assay of FV520B stainless steel.
Form of supply
stainless steel bar FV520B
For Details, please Contact